ENERGETIC BIOCIDAL MATERIALS AND SPORE NEUTRALIZATION

The objective of this dissertation is to explore a more accurate and versatile approach to investigating the neutralization of spores suffered from ultrafast heating and biocide based stresses, and further to explore and understand novel methods to supply ultrafast heating and biocides through nanostructured energetic materials A surface heating method was developed to apply accurate (± 25 ˚C), high heating rate thermal energy (200 - 800 ˚C, ~103 - ~105 ˚C/s). Uniform attachment of bacterial spores was achieved electrophoretically onto fine wires in liquids, which could be quantitatively detached into suspension for spore enumeration. The spore inactivation increased with temperature and heating rate, and fit a sigmoid response. The neutralization mechanisms of peak temperature and heating rate were correlated to the DNA damage at ~104 ˚C/s, and to the coat rupture by ultrafast vapor pressurization inside spores at ~105 ˚C/s. Humidity was found to have a synergistic effect of rapid heating and chlorine gas to neutralization efficiency. The primary neutralization mechanism of Cl2 and rapid heat is proposed to be chlorine reacting with the spore surface. The stress-kill correlation above provides guidance to explore new biocidal thermites, and to probe mechanisms. Results show that nano-Al/K2S2O8 released more gas at a lower temperature and generated a higher maximum pressure than the other nano-Al/oxysalts. Given that this thermite formulation generates the similar amount of SO2 as O2, it can be considered as a potential candidate for use in energetic biocidal applications. The reaction mechanisms of persulfate and other oxysalts containing thermites can be divided into two groups, with the reactive thermites (e.g. Al/K2S2O8) that generate ~10× higher of pressure and ~10× shorter of burn time ignited via a solid-gas Al/O2 reaction, while the less reactive thermites (e.g. Al/K2SO4) following a condensed phase Al/O reaction mechanism. These different ignition mechanisms were further re-evaluated by investigating the roles of free and bound oxygen. A constant critical reaction rate for ignition was found which is independent to ignition temperature, heating rate and free vs. bound oxygen.

Mitigation of High Alkalinity in Leachates of Aged Steel Slag

Steel slag, an abundant by-product of the steel-making industry, after it is aged, has a huge potential for use as an aggregate in road construction. However, the high pH of steel slag seepage (pH≥12) is a major impediment in its beneficial use. Analyses on aged steel slag samples demonstrated that the alkalinity producing capacity of aged steel slag samples strongly correlated to Ca(OH)2 dissolution and that prolonged aging periods have marginal effects on overall alkalinity. Treatment methods that included bitumen-coating, bathing in Al(III) solutions and addition of an alum-based drinking water treatment residual (WTR) were evaluated based on reduction in pH levels and leachate alkalinity. 10% (wt./wt.) alum-based drinking water treatment residual (WTR) addition to slag was determined to be the most successful mitigation method, providing 65−70% reduction in alkalinity both in batch-type and column leach tests, but final leachate pH was only 0.5−1 units lower and leachates were contaminated by dissolved Al(+III) (≥3−4 mM). Based on the interpretation of calculated saturation indices and SEM and EDX analyses, formation of calcium sulfoaluminate phases (i.e., ettringite and monosulfate) was suggested as the mechanism behind alkalinity mitigation upon WTR-modification. The residual alkalinity in WTR-amended slag leachates was able to be completely eliminated utilizing a biosolids compost with high base neutralization capacity. In column leach tests, effluent pH levels below 7 were maintained for 58−74 pore volumes worth of WTR-amended slag leachate using 0.13 kg compost (dry wt.) per 1 kg WTR-amended slag on average; also, dissolved Al(+III) was strongly retained on the compost.